Nagai, Takayuki; Okamoto, Yoshihiro; Akiyama, Daisuke*; Uehara, Akihiro*; Fujii, Toshiyuki*; Sekimoto, Shun*
KURNS Progress Report 2019, P. 257, 2020/08
To understand the influence of glass structural change by neutron irradiation and boron isotope composition, glass samples were made from enrichment boric acid reagents and neutron irradiation of those samples was carried out in Pn-2 of KUR. The structural change of glass sample after the irradiation will be estimated in 2020FY. Before neutron irradiation test of glass samples, the Si-O bridging structure difference by boron isotope composition compared by using a Raman spectrometry.
Nagai, Takayuki; Kobayashi, Hidekazu; Okamoto, Yoshihiro; Akiyama, Daisuke*; Sato, Nobuaki*; Uehara, Akihiro*; Fujii, Toshiyuki*; Sekimoto, Shun*
KURNS Progress Report 2018, P. 105, 2019/08
To understand this structural change of a borosilicate glass by a neutron irradiation in detail, the irradiation test was carried out in KUR in 2017FY. The glass structure was estimated by using Raman spectrometry in 2018FY. Comparing with the Raman spectra of glass samples before and after irradiation, it could be observed the change of peak height of Si-O bridging structure by the irradiation.
Nagai, Takayuki; Uehara, Akihiro*; Fujii, Toshiyuki*
KURRI Progress Report 2017, P. 128, 2018/08
In this study, to understand the structural change of a borosilicate glass by a neutron irradiation in detail, the neutron irradiation test was carried out for 50 min in the Pn-2 of the Kyoto University Research Reactor (KUR). The structural change of glass sample after the irradiation will be estimated in 2018FY. Before the irradiation test, the glass composition was selected to estimate a structural change accurately by Raman spectrometry and 2 kinds of Li free borosilicate glass for the irradiation test samples were prepared.